标准 |
牌号 |
抗拉强度(MPA) |
屈服强度(MPA) |
ASTM A106 |
A |
≥330 |
≥205 |
B |
≥415 |
≥240 | |
C |
≥485 |
≥275 |
标准 |
牌号 |
化学成分 | |||||||||
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Cu |
Ni |
V | ||
ASTM A106 |
A |
≤0.25 |
≥0.10 |
0.27~0.93 |
≤0.035 |
≤0.035 |
≤0.40 |
≤0.15 |
≤0.40 |
≤0.40 |
≤0.08 |
B |
≤0.30 |
≥0.10 |
0.29~1.06 |
≤0.035 |
≤0.035 |
≤0.40 |
≤0.15 |
≤0.40 |
≤0.40 |
≤0.08 | |
C |
≤0.35 |
≥0.10 |
0.29~1.06 |
≤0.35 |
≤0.35 |
≤0.40 |
≤0.15 |
≤0.40 |
≤0.40 |
≤0.08 |
标准 |
牌号/抗拉强度(Mpa) |
屈服强度(Mpa) |
伸长率(%) | |
5310-95 |
20G |
410~550 |
≥ 245 |
≥ 24 |
25MnG |
≥ 415 |
≥ 240 |
≥ 22 | |
15MoG |
450~600 |
≥ 270 |
≥ 22 | |
15CrMoG |
440~640 |
≥ 235 |
≥ 21 | |
12Cr2MoG |
450~600 |
≥ 280 |
≥ 20 | |
12Cr1MoVG |
470~640 |
≥ 255 |
≥ 21 |
标准 |
牌号 |
化学成分 | |||||||||
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Cu |
Ni |
| ||
GB5310 |
20G |
0.17-0.24 |
0.17-0.37 |
0.35-0.65 |
≤0.030 |
≤0.030 |
/ |
/ |
≤0.20 |
≤0.25 |
/ |
20MnG |
0.17-0.24 |
0.17-0.37 |
0.70-1.00 |
≤0.030 |
≤0.030 |
/ |
/ |
≤0.20 |
≤0.25 |
/ | |
15MoG |
0.12-0.18 |
0.17-0.37 |
0.40-0.80 |
≤0.030 |
≤0.030 |
/ |
0.25-0.35 |
≤0.20 |
≤0.30 |
/ | |
15CrMoG |
0.12-0.18 |
0.17-0.37 |
0.40-0.70 |
≤0.030 |
≤0.030 |
0.80-1.10 |
0.40-0.55 |
≤0.20 |
≤0.30 |
/ | |
12Cr2MoG |
0.08-0.15 |
≤0.50 |
0.40-0.70 |
≤0.030 |
≤0.030 |
2.00-2.50 |
0.90-1.20 |
≤0.20 |
≤0.30 |
/ | |
12Cr1MoVG |
0.08-0.15 |
0.17-0.37 |
0.40-0.70 |
≤0.030 |
≤0.030 |
0.90-1.20 |
0.25-0.35 |
≤0.20 |
≤0.30 |
0.15-0.35 |